Ocel 30 G (30Г1)

Ocel 06Х1 Ocel 06Х1Ф Ocel 06ХГР Ocel 06ХФ Ocel 07Х3ГНМЮА Ocel 08ГДНФ (SL-2; 08ГДНФЛ) Ocel 08Х2Г2ФА Ocel 08ХМФЧА (08ХМФЧ) Ocel 08ХМЧА (08ХМЧ) Ocel 09ГСФА (09ГСФ) Ocel 09Н2МФБА (09Н2МФБА-A) Ocel 09СФА (09СФ) Ocel 09ХГ2НАБч Ocel 09ХН2МД (АБ2-Ш1) Ocel 09ХН3МД (АБ3) Ocel 09ХН4МД (АБ4) Ocel 10Г2 (10Г2А) Ocel 10ГН (10ГНА) Ocel 10Х1С2М Ocel 10Х2ГНМ (10Х2ГНМА) Ocel 10Х2М1 (10Х2М1А) Ocel 10Х3ГНМЮА Ocel 10ХН3МД (АБ2-Ш2) Ocel 12Г1Р Ocel 12Х2Н4А (ЭИ83) Ocel 12Х2НВФА (ЭИ712) Ocel 12Х2НВФМА (ЭП506; ЭИ712М) Ocel 12Х2НМ1ФА Ocel 12Х2НМФА Ocel 12ХГН2МФБДАЮ (NE-4) Ocel 12ХГНМ Ocel 12ХГНМФ Ocel 12ХН Ocel 12ХН2 Ocel 12ХН2А Ocel 12ХН2МД (АБ1) Ocel 12ХН3А Ocel 12ХН3МД (АБ2; 12ХН3МДФ) Ocel 12ХН4МБД (АБ2Р) Ocel 138 Z-2 Ocel 13Н2ХА Ocel 13Н5А Ocel 13Х3НВМ2Ф (ДИ45; BKC-4) Ocel 13ХГМРБ Ocel 13ХГН2МД Ocel 13ХГН2МФД Ocel 13ХГСН1МД Ocel 13ХФА (13ХФ) Ocel 14Н2МФД (14Н2МФДА) Ocel 14Х2ГМР Ocel 14Х2Н3МА Ocel 14Х3ГМЮ Ocel 14ХГ2САФД Ocel 14ХГН Ocel 14ХГН2МДАФБ (14ХГНМДАФБ) Ocel 14ХГНМДАФБРТ (14ХГНМД) Ocel 14ХГСН2МА (ЭП176; ДИ3А) Ocel 14ХН3МА Ocel 15 G (15Г1) Ocel 15ГЮТ Ocel 15Н2М (15НМ) Ocel 15Н3МА Ocel 15Х Ocel 15Х1СМФБ Ocel 15Х2ГН2ТА Ocel 15Х2ГН2ТРА Ocel 15ХА Ocel 15ХГН2МАФАч Ocel 15ХГН2ТА (15ХГНТА) Ocel 15ХГНМ (15ХГНМА) Ocel 15ХМФА (15ХМФ) Ocel 15ХН3 Ocel 15ХР Ocel 15ХСМФБ (ЭП79) Ocel 15ХФА (15ХФ) Ocel 16Г2 Ocel 16Х2Н3МФБАЮ (16Х2Н3МФАБ; ВКС7) Ocel 16Х3НВФМБ (BKC-5; ДИ39) Ocel 16ХГ (АЦ16ХГ) Ocel 16ХГТА (ЭИ274) Ocel 16ХН3МА Ocel 16ХСН Ocel 17Н3МА Ocel 17ХГ Ocel 18Г2ХФЮД Ocel 18Х2Н4ВА Ocel 18Х2Н4МА Ocel 18ХГ Ocel 18ХГН2МФБ Ocel 18ХГТ Ocel 18ХН2Т Ocel 18ХН3МА Ocel 18ХНВА Ocel 18ХНМФД (18ХНМФДА) Ocel 19Х2НВФА (ЭИ763) Ocel 19Х2НМФА Ocel 19ХГН Ocel 19ХГНМА (19ХГНМ) Ocel 19ХГС Ocel 20 G (20Г1) Ocel 20Г2 Ocel 20Г2АФ (20Г2АФпс) Ocel 20Г2Р Ocel 20ГЮТ Ocel 20Н2М (20НМ) Ocel 20Ф (20ФА) Ocel 20Х Ocel 20Х2МА Ocel 20Х2МФА Ocel 20Х2Н4А Ocel 20Х2Н4МФ (20Х2Н4МФА) Ocel 20Х3НМФ (20Х3НМФА) Ocel 20ХГНМ Ocel 20ХГНМТ (20ХГНМТА) Ocel 20ХГНР Ocel 20ХГНТР Ocel 20ХГР Ocel 20ХГСА Ocel 20ХГСР Ocel 20ХМ Ocel 20ХН Ocel 20ХН2М (20ХНМ) Ocel 20ХН3А Ocel 20ХН3МФА (20ХН3МФ) Ocel 20ХН4ФА Ocel 20ХНР Ocel 20ХФА (20ХФ) Ocel 21Н5А (ЭИ56) Ocel 21Х2НВФА Ocel 21Х2НМФА Ocel 22ХГНМА (22ХГНМ) Ocel 22ХНМ Ocel 23Г2Д Ocel 23Х2НВФА (ЭИ659) Ocel 23Х2НМФА Ocel 23ХН2М Ocel 24Г2 Ocel 24Х3МФ (24Х3МФА) Ocel 24ХНМ Ocel 25G (25Г2) Ocel 50 G Ocel 50Г2 Ocel 50Х Ocel 50ХН Ocel 5ХНМ2 Ocel 85ГФ Ocel АК32 Ocel АК33 Ocel АК34 Ocel АК35 Ocel АК36 Ocel АК37 Ocel АК48 Ocel АК49 Ocel АК50 Ocel 25Н Ocel 25Н3А Ocel 25Х2Н4ВА Ocel 25Х2Н4МА Ocel 25ХГ2СФР Ocel 25ХГМ Ocel 25ХГНМА (25ХГНМ) Ocel 25ХГНМТ (25ХГНМТА) Ocel 25ХГСА Ocel 25ХГТ Ocel 25ХМ Ocel 25ХН3 Ocel 25ХНТЦ Ocel 26Г1 Ocel 26Х1МА (26Х1М) Ocel 26Х2НВМБР (КВК-26) Ocel 26ХГМ Ocel 26ХГМФ (26ХГМФА) Ocel 26ХМА (26ХМ; 25ХМ) Ocel 27ХГР Ocel 30 G (30Г1) Ocel 30Г1Р Ocel 30Г2 Ocel 30Т Ocel 30Х Ocel 30Х2Н2ВФА Ocel 30Х2Н2ВФМА Ocel 30Х2НВА Ocel 30Х2НВФА Ocel 30Х2НВФМА Ocel 30Х2НМА Ocel 30Х2НМФА (30Х2НМФ) Ocel 30Х3МФ Ocel 30Х3МФСА Ocel 30Х3НВА Ocel 30ХГС Ocel 30ХГСА Ocel 30ХГТ Ocel 30ХМ Ocel 30ХМА Ocel 30ХН2ВА Ocel 30ХН2ВФА Ocel 30ХН2МА (30ХНМА) Ocel 30ХН2МФА Ocel 30ХН3А Ocel 30ХН3М Ocel 30ХНМФА (30ХНВФА) Ocel 30ХРА Ocel 30ХСНВФА (ВП30) Ocel 32Г2 Ocel 32Г2С Ocel 32Х2НВМБР (КВК-32) Ocel 33Х3СНМВФА (СП33; ЭП613) Ocel 33ХН3МА Ocel 33ХС Ocel 34ХН1ВА (0ХН1В) Ocel 34ХН3М Ocel 35Г Ocel 35Г1Р Ocel 35Г2 Ocel 35Х Ocel 35Х2ГЮФ Ocel 35ХГН2 Ocel 35ХГСА Ocel 35ХМ Ocel 35ХН2Ф Ocel 35ХН3МА (35ХН3М) Ocel 36Г2С Ocel 36Г2СР Ocel 36Х2Н2МФА (36ХН1МФА) Ocel 37Г2С Ocel 37Х2НВМБР (КВК-37) Ocel 37ХН3А Ocel 38Х2МЮА (38ХМЮА) Ocel 38Х2Н2ВА Ocel 38Х2Н2МА (38ХНМА) Ocel 38Х2Н3М Ocel 38Х2НМ Ocel 38Х2НМФ Ocel 38Х2Ю (38Х2ЮА) Ocel 38ХА Ocel 38ХГМ Ocel 38ХГН Ocel 38ХГНМ Ocel 38ХГСА (38ХГС) Ocel 38ХМ (42ХМ) Ocel 38ХМА Ocel 38ХН3ВА Ocel 38ХН3МА Ocel 38ХС Ocel 38ХФР (40ХФР) Ocel 40 G Ocel 40Г2 Ocel 40ГР (40Г1Р) Ocel 40Х (40ХА) Ocel 40Х2Н2ВА Ocel 40Х2Н2МА Slitina 40Х3М2ФА (USP-40) Ocel 40ХГНМ Ocel 40ХГСМА Ocel 40ХГТР Ocel 40ХМФА (40ХМФ) Ocel 40ХН Ocel 40ХН2ВА (40ХНВА) Ocel 40ХН2МА (40ХНМА) Ocel 40ХР Ocel 40ХС Ocel 40ХСН2МА Ocel 40ХФА (40ХФ) Ocel 42Х2НВМБР (КВК-42) Ocel 42Х2НМБР (АБО70Н) Ocel 42ХМФА (42ХМФ) Ocel 44Х2НМБР (АБО70В) Ocel 45Г Ocel 45Г2 Ocel 45Х Ocel 45ХН Ocel 45ХН2МФА (45ХНМФА) Ocel 47ГТ Ocel 48ХН3М

Označení

Název Význam
Označení GOST cyrilice 30Г
Označení GOST rumunština 30G
Транслит 30G
Na chemické prvky 30Mn
Název Význam
Označení GOST cyrilice 30Г1
Označení GOST rumunština 30G1
Транслит 30G1
Na chemické prvky 30Mn1

Popis

Ocel 30 G platí: pro výrobu улучшаемых detailů, které jsou pro požadavky nízké pevnosti (тяг, nápravy, válce, disky, šrouby, matice, šrouby a další díly); vysílat polotovary používané pro výrobu trubek a železnou tyčí; bandpass pronájmu, použije pro výrobu součástek automobilů.

Poznámka

Ocel konstrukční jakostní марганцовистая.

Standardy

Název Kód Standardy
Kovy a kovové výrobky В32 GOST 1051-73, GOST 4543-71, GOST 7417-75, GOST 8559-75, GOST 8560-78, GOST 14955-77, GOST 1050-2013, TU 14-1-2118-77, TU 14-11-245-88, TU 14-1-1271-75, TU 14-136-367-2008
Kovy a kovové výrobky В22 GOST 1133-71, GOST 8278-83, GOST 8281-80, GOST 8282-83, GOST 8283-93, GOST 8319.0-75, GOST 9234-74, GOST 11474-76, GOST 2590-2006, GOST 2591-2006, GOST 2879-2006
Plechy a pásy В33 GOST 1577-93, TU 14-1-522-93, TU 14-1-522-73
Plechy a pásy В23 GOST 82-70, GOST 19903-74, GOST 103-2006, GOST 19903-90
Blanks. Sochory. desky В31 OST 3-1686-90, TU 14-1-4944-90, TU 14-1-4992-91
pásky В34 TU 14-1-1815-76, TU 14-4-156-72

Chemické složení

Standard C S P Mn Cr Si Ni Fe Cu V Ti Mo Sn W
TU 14-1-4944-90 0.29-0.33 ≤0.03 ≤0.03 1.2-1.4 ≤0.2 0.15-0.3 ≤0.3 Zbytek ≤0.25 ≤0.05 - ≤0.06 ≤0.02 -
GOST 4543-71 0.27-0.35 ≤0.035 ≤0.035 0.7-1 ≤0.3 0.17-0.37 ≤0.3 Zbytek ≤0.3 ≤0.05 ≤0.03 ≤0.15 - ≤0.2
Fe - základ.
V souladu s GOST 4543-71 chemického složení jsou uvedeny pro ocelové 30G. Regulovaný obsah v oceli: P≤0,025%; S≤0,025%; Su≤0,30%; osobovysokokachestvennoy v oceli: P≤0,025%; S≤0,015%; Su≤0,25%.
Tu 14-1-4944-90 chemické sloučeniny jsou uvedeny pouze pro ocelové 30G1. Tolerance k obsahu jednotlivých prvků v souladu s GOST 4543 a GOST 19821.

Mechanické vlastnosti

Průřez, mm t отпуска, °C sT|s0,2, Mpa σB, Mpa d5, % y, % kj/m2, кДж/м2 HRC
Pás je ve stavu dodání (bez tepelného zpracování v травленом stavu), na druhé 14-1-522-93
- - ≥315 ≥540 ≥20 - - -
Páska. Zpevnění na vzduchu s 810-820 °C + Dovolená při 400 °C, chlazení na vzduchu
≤3 - - ≥1130 6-7 - - 37
Odrůdy pronájem. Zpevnění ve vodě s 840 °C + Dovolená při 550 °C (uvedeno místo svíčkové vzorků)
120 - ≥540 ≥710 ≥21 ≥63 ≥1470 -
Tyč průřezu 70 mm. Zpevnění na olej s 850 °C + Dovolenou (podélné vzorky)
- 300 ≥540 ≥780 ≥20 ≥45 ≥390 -
Odrůdy pronájem. Normalizace při 900 °C, chlazení na vzduchu + Dovolená při 680-710 °C (podélné vzorky)
- - ≥370 ≥710 ≥20 ≥32 - -
Odrůdy pronájem. Zpevnění ve vodě s 840 °C + Dovolená při 550 °C (uvedeno místo svíčkové vzorků)
160 - ≥530 ≥700 ≥22 ≥63 ≥1370 -
Tyč průřezu 70 mm. Zpevnění na olej s 850 °C + Dovolenou (podélné vzorky)
- 400 ≥540 ≥760 ≥20 ≥52 ≥290 -
Odrůdy pronájem. Normalizace při 900 °C, chlazení na vzduchu + Dovolená při 680-710 °C (podélné vzorky)
- - ≥330 ≥630 ≥29 ≥46 - -
Odrůdy pronájem. Zpevnění ve vodě s 860 °C + Dovolená při 600 °C, chlazení na vzduchu
25 - ≥315 ≥540 ≥20 ≥45 ≥780 -
Odrůdy pronájem. Zpevnění ve vodě s 840 °C + Dovolená při 550 °C (uvedeno místo svíčkové vzorků)
40 - ≥590 ≥740 ≥22 ≥65 ≥1570 -
Tyč průřezu 70 mm. Zpevnění na olej s 850 °C + Dovolenou (podélné vzorky)
- 500 ≥490 ≥700 ≥21 ≥59 ≥490 -
Odrůdy pronájem. Normalizace při 900 °C, chlazení na vzduchu + Dovolená při 680-710 °C (podélné vzorky)
- - ≥305 ≥590 ≥21 ≥41 - -
Odrůdy pronájem. Zpevnění ve vodě s 840 °C + Dovolená při 550 °C (uvedeno místo svíčkové vzorků)
80 - ≥560 ≥730 ≥21 ≥64 ≥1570 -
Tyč průřezu 70 mm. Zpevnění na olej s 850 °C + Dovolenou (podélné vzorky)
- 600 ≥440 ≥640 ≥25 ≥69 ≥1170 -
Odrůdy pronájem. Zpevnění ve vodě s 840 °C + Dovolená při 550 °C (uvedeno místo svíčkové vzorků)
120 - ≥490 ≥600 ≥22 - ≥980 -
160 - ≥490 ≥590 ≥23 - ≥980 -
200 - ≥450 ≥600 ≥27 ≥63 ≥880 -
40 - ≥540 ≥710 ≥25 - ≥1370 -
80 - ≥490 ≥650 ≥24 - ≥1080 -

Popis mechanických označení

Název Popis
Průřez Section
sT|s0,2 Mez průtažnosti nebo proporcionální mez tolerance na trvalé deformace - 0,2%
σB Limit krátkodobého pevnost
d5 Prodloužení po rozchodu
y Relativní zúžení
kj/m2 Rázová houževnatost
HRC Tvrdost podle Роквеллу (индентор diamond, сфероконический)

Fyzikální vlastnosti

Teplota Е, ГПа r, кг/м3 l, Вт/(м · °С) a, 10-6 1/°С С, Дж/(кг · °С)
20 204 7810 - - -
100 - - 76 126 470
200 - - 65 139 483
300 - - 53 146 546
400 - - 44 15 601
500 - - 38 155 601
600 - - - 156 -
700 - - - 156 864
900 - - - 148 -

Popis fyzické notace

Název Popis
Е Modul normální pružnosti
G Modul pružnosti při přesunu кручением
r Hustota
l Faktor pronikání tepla
R Ud. электросопротивление

Technologické vlastnosti

Název Význam
svařitelnost Omezeně свариваемая ocel. Způsoby svařování: RDS, TD, pod tavidlem. Doporučuje se vyhřívání a následné tepelné zpracování. CCC bez omezení.
Tendence zmírnit křehkost Je náchylná při 1,0 % Mn.
teplota kování Start - 1250 °C, na konci - 800 °C. průřez Obrobku až 400 mm jsou chlazeny ve vzduchu.
vločky není citlivý.
obrobitelnost V нормализованном stavu při НВ 149-197 Kn televize.cpf.=1,00 Kn b.čl.=0,80.
mikrostruktura Hodnota аустенитного zrna v oceli by neměla být větší než 5 pokojů na GOST 5639. Hloubka обезуглероженного vrstvy na oceli pás o tloušťce 3 až 4 mm by neměla být větší než 0,08 mm (3%), tloušťky přes 4 do 7 mm včetně - ne více než 0,16 mm (2%).

Náš konzultant vám ušetří čas

+49(1516) 758 59 40
Telegram:
WhatsApp:

Předplatné

Speciální akce a slevy. :)